Tensile Strength of Human Pericardium Treated with Glutaraldehyde
Hiromasa YamashitaShigeyuki OzakiKiyotaka IwasakiIsamu KawaseYukinari NozawaMitsuo Umezu
Author information
JOURNAL FREE ACCESS

2012 Volume 18 Issue 5 Pages 434-437

Details
Abstract

Purpose: We have reconstructed aortic valves using autologous pericardium treated with glutaraldehyde since April 2007. However, the strength of the human pericardium has not been confirmed. We compared tensile strength between glutaraldehyde-treated human pericardium and aortic valve leaflets with various degrees of calcification to determine their suitability for use in aortic valve reconstruction.
Methods: We measured the ultimate tensile strength and elasticity of samples of glutaraldehyde-treated pericardia (n = 8), non-calcified (n = 12), calcified (n = 9) and decalcified (n = 21) aortic leaflets collected from 23 patients who underwent aortic valve surgery. Aortic valves were decalcified using a cavitational ultrasonic surgical aspirator. The pericardium was immersed in 0.6% buffered glutaraldehyde for 10 minutes and then rinsed three times for 6 minutes each in normal saline.
Results: The ultimate tensile strength of the glutaraldehyde-treated human pericardium, non-calcified, calcified and decalcified leaflets was 10, 2.8, 1.0 and 0.8 MPa, respectively.
Conclusions: The ultimate tensile strength of glutaraldehyde-treated human pericardium was 4 times higher than non-calcified leaflets, indicating its suitability for application to aortic valve reconstruction. Calcified leaflets were slightly stronger than decalcified leaflets. Thus, calcification can be removed without altering the tensile strength of valve materials.

Content from these authors
© 2012 The Editorial Committee of Annals of Thoracic and Cardiovascular Surgery

This article is licensed under a Creative Commons [Attribution-NonCommercial-NoDerivatives 4.0 International] license.
https://creativecommons.org/licenses/by-nc-nd/4.0/
Previous article Next article
feedback
Top