Afterglow luminance property of phosphorescent phosphor SrAl2O4:Eu2+,Dy3+-glass composites
Hideki YOSHIDAShigeru FUJINOToshihisa KAJIWARA
Author information
JOURNAL FREE ACCESS

2010 Volume 118 Issue 1381 Pages 784-787

Details
Abstract

The effect of mixing ratio, firing temperature and matrix glass composition on afterglow luminance property of SrAl2O4:Eu2+,Dy3+-glass composites were investigated. As a result, the brightness showed a maximum at 35 mass % of the mixing ratio of the phosphor for the glass and 780°C of the firing temperature. And it was increased with decreasing the Na2O content of the matrix glass. From the backscattered electron and the EDX analysis, it is thought that the intermediate layers generated between the phosphors and the Na2O-poor matrix glass work as antireflective and the phosphor particles in the composite emit phosphorescent light more efficiently. As higher the basicity parameter, B, the intermediate layer was clearer, which means that the reactivity at the phosphor/glass boundaries was lower, and the narrow reaction layers was formed.

Content from these authors
© 2010 The Ceramic Society of Japan
Previous article Next article
feedback
Top